| Alloy Name | |
| UNS | C12000 |
| ISO | Cu-DHP |
| JIS | C1201 |
We are producing varied range of copper cold rolled products with highest purity in various in chemical compositions, sizes and specifications, which are suitable for various final processing and finish products. .
Cu-DHP is a phosphorus-deoxidized copper with a limited, medium Amount of residual Phosphorus. It has a good electrical conductivity and excellent welding and soldering properties. It can be formed excellent, either hot or cold.
| Chemical Composition | Weight percentage |
| Cu | 99.80 Min % |
| P | 0.15-0.04 % |
| Main Applications |
| Industrial : Tubing, LP Gas Service, Conductors, Resistance Welding Equipment, Welded Tube, Medical Gas- Oxygen |
| Other : Applications Requiring Welding or Brazing, Apparatus industry |
| Physical Properties Typical values in annealed temper at 20 °C | ||
| Density | 8.94 | g/cm3 |
| Thermal expansion coefficient -191 .. 16 | 14.1 | 10-6/K |
| Specific heat capacity - 0 .. 300°C | 17.7 | 10-6/K |
| Thermal conductivity | 0.386 | J/(g•K) |
| Electrical conductivity (1 MS/m = 1 m/(O mm²) | 350 | W/(m•K) |
| Electrical conductivity (IACS) | 52.2 | MS/m % |
| Thermal coefficient of electrical resistance (0 .. 200 C) | 3.6 | 10-3/K |
| Modulus of elasticity ( 1 GPa = 1 kN/mm²) cold formed | 118 | GPA |
Resistant to: Atmospheric corrosion: formation of the a greenish protective patina due to the formation of copper basic salts (such sulphates, chlorides in marine environment, nitrates and carbonates). Cu-DHP has a good resistance in natural and industrial atmosphere. Industrial and drinking water, aqueous and alkaline solutions (not oxidizing), pure water vapor (steam), non oxidizing acids (without oxygen in solution) and salts, neutral saline solutions. Practically resistant against stress corrosion cracking .
| Mechanical Properties (EN 1652) | ||||
| Temper | Tensile Strength Rm MPa (N/mm2) |
Yield Strength Rp0.2 MPa (N/mm2) |
Elongation A50mm % | Hardness HV |
| O (SOFT) | 210 Min | 35 Min | 60 Max | |
| HB (half Hard) | 240 min | 180 | 10 Min | 70 to 95 |
| HD (Hard) | 290 min | 250 | 4 Min | 90 min |